3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: [email protected] or [email protected]
There are CAD communities available at: [email protected] or [email protected]
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
Be respectful, especially when disagreeing. Everyone should feel welcome here.
No porn (NSFW prints are acceptable but must be marked NSFW)
No Ads / Spamming / Guerrilla Marketing
Do not create links to reddit
If you see an issue please flag it
No guns
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
This is the temp tower of my wood print experiment Cand even se much difference. It goes from 260 to 190. Below 225 gets really flimsy and above 240 melts. But even 230, the "best" one is really bad, and I'm not talking about retraction. Even the layers that melt are inconsistent.
Also it's not humidity since the filament was in a filament dryer for.16hours.
edit: The nozzle is 0.8
can someone think of anything else?
I don't know what your setup is but that looks to me like you need a higher flow melt zone and better extruder grip. I was able to get out of a similar situation with particle filled filaments using this: https://kevinakasam.com/papilio/ and further improvement with a hall effect filament width sensor but the tinkering for that was an actual nightmare.
wood filament is also just cursed. the improvement to regular filament was much better while the particle filaments just went from similr to your wood filament to tolerable.
oh that's interesting my extruder is indeed kind of shitty. I'll take a look at this thanks